When I went to glass it took me an embarrassingly long time to realize I needed to up my bed temp by 10° if I wanted good adhesion

I swapped to glass a few years ago and the things I have learned since are that glass that’s too thick will cause you issues with bed temperature, and you can print PETG on it so long as you can guarantee you’ll be there when the print finishes to release it with IPA or you’ll have chunks of glass missing from your build plate. I got a G10 build plate 2 days ago and sofar I’m liking it more than glass